..:: Chemicals Compositions ::..

 
GRADE %C %Mn %Si %P %S %Ni %Cr %Cu %Mo N2 ppm Others Remarks
17-4PH 0.025 0.60 0.30 0.000 0.010 4.20 15.10 3.10 0.00 200   Nb+Ta=
  0.045 0.80 0.40 0.040 0.020 4.40 15.50 3.30 0.20 350   0.25/0.30
201E 0.080 7.50 0.40 0.000 0.000 3.30 15.60 0.00 0.00 1700    
  0.100 8.00 0.60 0.060 0.010 3.50 16.00 0.30 0.30 1900    
201M 0.080 7.50 0.50 0.000 0.000 3.10 16.10 0.30 0.00 1700    
  0.100 8.00 0.70 0.060 0.010 3.40 16.40 0.50 0.30 1900    
201S 0.080 8.20 0.40 0.000 0.000 0.30 14.00 1.70 0.00 1500   Aim Ni eqv >12
  0.100 8.50 0.60 0.080 0.015 0.50 14.50 1.90 0.30 1700    
201WR06 0.080 8.10 0.40 0.000 0.000 0.60 14.00 1.70 0.00 1500   Aim Ni eqv >12
  0.100 8.30 0.60 0.080 0.015 0.80 14.50 1.90 0.30 1700    
201WR09 0.080 8.10 0.40 0.000 0.000 0.90 14.00 1.70 0.00 1400 Aim Ni eqv >12
  0.100 8.30 0.60 0.080 0.015 1.10 14.50 1.90 0.30 1600    
201WR2 0.060 8.10 0.40 0.000 0.000 2.00 14.50 1.60 0.00 1300    
  0.080 8.30 0.60 0.070 0.015 2.20 14.80 1.80 0.30 1500    
201WR3 0.040 8.30 0.40 0.000 0.000 3.05 14.50 1.70 0.00 1300    
  0.060 8.60 0.60 0.070 0.010 3.30 15.00 1.90 0.30 1500    
201WR3HS 0.040 8.30 0.40 0.000 0.015 3.05 14.50 1.70 0.00 1300    
  0.060 8.60 0.60 0.070 0.030 3.30 15.00 1.90 0.30 1500    
201WR 0.080 8.20 0.40 0.000 0.000 0.30 14.00 1.70 0.00 1500   Aim Ni eqv >12
  0.100 8.50 0.60 0.080 0.015 0.50 14.50 1.90 0.30 1700    
302 0.080 1.10 0.25 0.000 0.000 8.10 18.00 0.00 0.00 500    
  0.100 1.30 0.45 0.040 0.010 8.20 18.30 0.30 0.30 700    
302BR 0.090 0.30 0.30 0.000 0.000 8.10 18.00 0.15 0.00 700    
  0.110 0.50 0.50 0.040 0.010 8.20 18.30 0.30 0.30 900    
302HQ 0.015 0.60 0.25 0.000 0.000 9.50 17.30 3.25 0.00 0    
  0.025 0.80 0.45 0.040 0.010 9.70 17.60 3.50 0.30 250    
302HQCr18 0.015 0.60 0.25 0.000 0.000 9.50 18.10 3.25 0.00 0    
  0.025 0.80 0.45 0.040 0.010 9.70 18.30 3.50 0.30 250    
302K 0.090 1.50 0.25 0.000 0.000 8.10 17.10 0.00 0.00 500    
  0.110 1.70 0.45 0.040 0.010 8.20 17.40 0.30 0.30 700    
302RR 0.070 0.50 0.30 0.000 0.000 8.20 18.10 0.00 0.00 600    
  0.090 0.75 0.50 0.040 0.010 8.40 18.50 0.30 0.30 800    
302V 0.060 0.30 0.30 0.000 0.000 8.10 18.10 0.00 0.00 600    
  0.080 0.50 0.45 0.040 0.010 8.20 18.30 0.30 0.30 800    
303Cu 0.035 1.90 0.25 0.000 0.280 8.50 17.20 2.00 0.00 400   CaSi inj must
  0.055 2.00 0.45 0.040 0.300 8.80 17.60 2.40 0.30 600    
303EHS 0.035 1.90 0.25 0.000 0.300 8.30 17.20 0.00 0.00 300   CaSi inj must
  0.055 2.00 0.45 0.040 0.330 8.60 17.60 0.30 0.30 500    
303NMHS 0.030 1.90 0.15 0.000 0.310 8.20 17.50 0.00 0.00 600   CaSi inj must
  0.050 2.00 0.30 0.040 0.340 8.40 17.90 0.30 0.30 800    
303NMHSCu 0.030 1.90 0.15 0.000 0.310 8.50 17.30 0.40 0.00 350   CaSi inj must
  0.050 2.00 0.30 0.040 0.340 8.70 17.70 0.60 0.30 550    
303PMS 0.050 1.90 0.25 0.000 0.280 8.60 17.20 0.30 0.00 0   CaSi inj must
  0.070 2.00 0.45 0.040 0.320 8.90 17.60 0.50 0.30 250    
303USA 0.020 1.90 0.30 0.000 0.240 8.90 17.20 0.00 0.00 0   CaSi inj must
  0.035 2.00 0.50 0.040 0.270 9.20 17.60 0.30 0.30 300   AIM S = 0.25 MAX
303V 0.030 1.90 0.25 0.000 0.310 8.10 17.10 0.00 0.00 300   CaSi inj must
  0.050 2.00 0.45 0.040 0.340 8.30 17.40 0.30 0.30 500    
303XM 0.035 1.90 0.25 0.000 0.310 8.90 17.20 0.40 0.00 0   CaSi inj must
  0.055 2.00 0.45 0.040 0.340 9.10 17.60 0.60 0.30 300    
304 0.050 1.30 0.25 0.000 0.000 8.00 18.10 0.00 0.00 400    
  0.070 1.50 0.45 0.040 0.015 8.10 18.40 0.30 0.30 600    
304Cu 0.050 1.30 0.30 0.000 0.000 8.00 18.10 0.40 0.00 400    
  0.070 1.50 0.50 0.040 0.015 8.20 18.40 0.60 0.30 600    
304E 0.040 1.40 0.25 0.000 0.000 8.60 18.10 0.00 0.00 400    
  0.060 1.60 0.45 0.040 0.020 8.80 18.30 0.30 0.30 600    
304ECu 0.020 1.60 0.25 0.000 0.000 8.70 18.40 0.90 0.00 0   CWH factor=
  0.028 1.80 0.45 0.040 0.010 9.00 18.80 1.10 0.30 250   94 -107
304ED 0.030 1.20 0.25 0.000 0.000 8.50 18.10 0.00 0.00 400    
  0.050 1.40 0.45 0.400 0.015 8.80 18.40 0.30 0.30 600    
304EHS 0.030 1.50 0.25 0.000 0.020 8.60 18.10 0.00 0.00 400   CaSi inj must
  0.050 1.70 0.45 0.040 0.030 8.80 18.30 0.30 0.30 600    
304EN 0.030 1.10 0.25 0.000 0.000 9.10 18.10 0.00 0.00 300    
  0.050 1.30 0.45 0.040 0.010 9.40 18.40 0.25 0.20 500    
304ENM 0.050 1.60 0.40 0.000 0.000 8.80 18.10 0.00 0.00 700    
  0.070 1.80 0.60 0.040 0.010 9.00 18.40 0.30 0.30 900    
304H 0.060 1.00 0.30 0.000 0.000 8.10 18.10 0.00 0.00 400    
  0.080 1.20 0.50 0.035 0.010 8.20 18.40 0.25 0.20 600    
304HC 0.025 1.40 0.25 0.000 0.000 8.20 18.10 2.20 0.00 300    
  0.045 1.60 0.45 0.040 0.020 8.40 18.40 2.40 0.30 500    
304HS 0.040 1.30 0.25 0.000 0.020 8.00 18.10 0.00 0.00 400   CaSi inj must
  0.060 1.50 0.45 0.040 0.030 8.10 18.40 0.30 0.30 600    
304HSP 0.045 1.00 0.30 0.000 0.000 9.60 18.10 0.00 0.00 0    
  0.065 1.20 0.50 0.040 0.010 9.90 18.40 0.25 0.20 200    
304HU 0.060 0.70 0.20 0.000 0.000 8.30 18.10 0.00 0.00 400    
  0.080 0.80 0.30 0.040 0.010 8.50 18.40 0.30 0.30 600    
304L 0.000 1.50 0.25 0.000 0.000 8.50 18.10 0.00 0.00 400    
  0.028 1.70 0.45 0.040 0.010 8.70 18.40 0.30 0.30 550    
304LAHS 0.000 1.60 0.25 0.000 0.015 8.10 18.10 0.00 0.00 600   CaSi inj must
  0.028 1.80 0.45 0.040 0.030 8.30 18.30 0.30 0.30 800    
304LC 0.000 1.60 0.30 0.000 0.010 8.90 18.50 0.00 0.00 600    
  0.028 1.80 0.50 0.040 0.020 9.20 18.90 0.30 0.30 800    
304LE 0.000 1.60 0.25 0.000 0.000 9.10 18.20 0.00 0.00 0   CaSi inj must
  0.028 1.80 0.45 0.040 0.010 9.40 18.40 0.30 0.30 250    
304LEHS 0.000 1.60 0.25 0.000 0.020 9.10 18.10 0.00 0.00 0   CaSi inj must
  0.028 1.80 0.45 0.040 0.030 9.40 18.40 0.30 0.30 250    
304LER 0.000 1.50 0.25 0.000 0.000 9.30 18.60 0.00 0.00 0   P+S= 0.03 max
  0.025 1.70 0.45 0.025 0.010 9.60 18.90 0.25 0.25 300    
304LHS 0.000 1.50 0.25 0.000 0.020 8.50 18.10 0.00 0.00 400   CaSi inj must
  0.028 1.70 0.45 0.040 0.030 8.70 18.40 0.30 0.30 600    
304LHSCu 0.000 1.50 0.25 0.000 0.020 8.50 18.10 0.40 0.00 400   CaSi inj must
  0.028 1.70 0.45 0.040 0.030 8.70 18.40 0.60 0.30 600    
304LMS 0.000 1.50 0.25 0.000 0.010 8.50 18.10 0.00 0.00 400   CaSi inj must
  0.028 1.70 0.45 0.040 0.020 8.70 18.30 0.30 0.30 600    
304LN 0.000 1.40 0.25 0.000 0.000 10.20 18.30 0.00 0.00 0    
  0.028 1.60 0.45 0.040 0.010 10.40 18.50 0.30 0.30 250    
304LNHS 0.000 0.70 0.25 0.000 0.020 10.20 18.30 0.00 0.00 0   CaSi inj must
  0.028 0.90 0.45 0.040 0.030 10.40 18.50 0.30 0.30 250    
304LNSP 0.020 1.00 0.30 0.000 0.000 10.10 18.30 0.00 0.00 0    
  0.028 1.20 0.45 0.028 0.010 10.40 18.70 0.30 0.15 250    
304LR 0.000 1.50 0.25 0.000 0.000 8.80 18.10 0.00 0.00 300    
  0.028 1.70 0.45 0.040 0.010 9.00 18.30 0.30 0.30 500    
304LRHS 0.000 1.30 0.30 0.000 0.020 9.10 18.10 0.00 0.00 400   CaSi inj must
  0.028 1.60 0.50 0.040 0.030 9.40 18.40 0.30 0.30 600    
304LU 0.000 1.20 0.30 0.000 0.000 9.50 18.10 0.40 0.30 0    
  0.028 1.40 0.50 0.040 0.010 9.70 18.40 0.60 0.50 300    
304M 0.040 0.80 0.25 0.000 0.000 9.10 18.10 0.00 0.00 300    
  0.060 1.00 0.45 0.040 0.010 9.30 18.40 0.30 0.30 500    
304ME 0.025 1.10 0.25 0.000 0.000 9.10 18.10 0.00 0.00 300   CaSi inj must
  0.045 1.30 0.45 0.035 0.010 9.40 18.40 0.30 0.30 500    
304MK 0.030 1.20 0.25 0.000 0.000 9.10 18.10 0.00 0.00 300    
  0.050 1.40 0.45 0.040 0.010 9.30 18.40 0.30 0.30 500    
304MU 0.040 1.60 0.20 0.000 0.000 8.10 18.10 0.00 0.00 400    
  0.060 1.80 0.30 0.040 0.010 8.40 18.40 0.30 0.30 600    
304NM 0.050 1.60 0.40 0.000 0.000 8.00 18.10 0.00 0.00 700    
  0.070 1.80 0.60 0.040 0.020 8.10 18.40 0.30 0.30 900    
304NMCU 0.050 1.60 0.40 0.000 0.000 8.00 18.10 0.70 0.00 600    
  0.070 1.80 0.60 0.040 0.010 8.10 18.40 0.90 0.30 800    
304NMHS 0.050 1.60 0.40 0.000 0.020 8.00 18.10 0.00 0.00 700   CaSi inj must
  0.070 1.80 0.60 0.040 0.030 8.20 18.40 0.30 0.30 900    
304NMHSCu 0.050 1.60 0.40 0.000 0.020 8.00 18.10 0.40 0.00 700   CaSi inj must
  0.070 1.80 0.60 0.040 0.030 8.10 18.40 0.60 0.30 900    
304S LP 0.040 1.40 0.25 0.000 0.000 8.10 18.10 0.00 0.00 400   Low Phosphorous
  0.060 1.60 0.45 0.025 0.015 8.20 18.40 0.30 0.30 600   Aim N2 =500 ppm
304S 0.040 1.40 0.25 0.000 0.000 8.10 18.10 0.00 0.00 400    
  0.060 1.60 0.45 0.040 0.015 8.20 18.40 0.30 0.30 600    
304SCu 0.050 1.40 0.25 0.000 0.000 8.00 18.10 0.40 0.00 600    
  0.070 1.60 0.45 0.040 0.010 8.20 18.40 0.60 0.30 800    
304SD 0.050 1.00 0.25 0.000 0.000 8.30 18.10 0.00 0.00 400    
  0.070 1.20 0.45 0.040 0.010 8.50 18.40 0.30 0.30 600    
304SDCu 0.050 1.00 0.25 0.000 0.000 8.20 18.00 0.60 0.00 300    
  0.070 1.20 0.45 0.040 0.010 8.40 18.40 0.90 0.30 500    
304SM 0.060 1.20 0.30 0.000 0.000 8.40 18.10 0.00 0.00 300    
  0.080 1.40 0.50 0.030 0.020 8.60 18.40 0.30 0.30 500    
304SR 0.040 1.40 0.25 0.000 0.000 8.10 18.10 0.00 0.00 400    
  0.060 1.60 0.45 0.040 0.015 8.20 18.40 0.30 0.30 600    
304V 0.030 1.50 0.20 0.000 0.000 8.00 18.10 0.00 0.00 400    
  0.050 1.70 0.30 0.040 0.015 8.10 18.40 0.30 0.30 600    
305 0.000 1.70 0.30 0.000 0.015 10.70 18.30 0.00 0.00 0   CaSi inj must
  0.025 1.90 0.50 0.040 0.025 10.90 18.60 0.30 0.30 250    
308LER Lsi-RR 0.000 1.60 0.10 0.000 0.000 9.80 19.60 0.00 0.00 500   P+S=0.03 max
  0.018 1.90 0.20 0.020 0.010 10.20 19.90 0.25 0.20 700    
308LER Lsi-VW 0.000 1.60 0.00 0.000 0.000 9.80 19.60 0.00 0.00 500   P+S= 0.03 max
  0.018 1.90 0.10 0.020 0.010 10.20 19.90 0.20 0.25 700   Co = 0.15 max
308LER Msi 0.000 1.60 0.35 0.000 0.000 10.10 19.60 0.00 0.00 400   P+S= 0.03 max
  0.018 1.90 0.45 0.020 0.010 10.30 19.80 0.15 0.20 600   Co = 0.15 max
309LER 0.000 1.70 0.30 0.000 0.000 13.70 23.10 0.00 0.00 500   P+S= 0.03 max
  0.018 1.90 0.45 0.020 0.010 13.90 23.40 0.25 0.20 700    
309S 0.015 1.60 0.25 0.000 0.000 13.60 22.10 0.35 0.00 350   CaSi inj must
  0.025 1.80 0.35 0.025 0.005 13.90 22.40 0.50 0.30 550    
310S 0.035 1.20 0.60 0.000 0.000 19.20 25.40 0.00 0.00 0    
  0.055 1.40 0.75 0.040 0.005 19.50 25.90 0.30 0.30 200    
314 0.015 1.45 2.30 0.000 0.000 19.90 23.00 0.00 0.00 0    
  0.035 1.65 2.50 0.030 0.010 20.30 23.60 0.30 0.10 300    
316(LowP) 0.040 1.30 0.30 0.000 0.000 10.10 16.50 0.00 2.02 400    
  0.060 1.50 0.45 0.025 0.010 10.30 16.70 0.30 2.20 600    
316 0.040 1.30 0.30 0.000 0.000 10.10 16.50 0.00 2.02 400    
  0.060 1.50 0.50 0.040 0.010 10.30 16.70 0.30 2.20 600    
316E 0.040 1.20 0.25 0.000 0.000 10.60 16.60 0.00 2.02 300    
  0.060 1.40 0.45 0.040 0.010 10.90 17.00 0.30 2.00 500    
316EHS 0.040 1.20 0.30 0.000 0.020 10.60 16.60 0.00 2.02 300   CaSi inj must
  0.060 1.40 0.50 0.040 0.030 10.90 17.00 0.30 2.00 500    
316EN 0.025 1.20 0.25 0.000 0.000 11.10 16.80 0.00 2.02 250    
  0.045 1.40 0.45 0.040 0.010 11.30 17.20 0.30 2.20 450    
316EP 0.040 1.20 0.25 0.000 0.000 10.60 16.80 0.00 2.02 300    
  0.060 1.40 0.45 0.040 0.015 10.90 17.20 0.30 2.20 500    
316ESPL 0.045 1.00 0.25 0.000 0.000 12.40 17.60 0.00 2.50 0    
  0.065 1.20 0.45 0.040 0.010 12.60 18.00 0.30 2.70 250    
316G 0.040 1.70 0.25 0.000 0.000 10.10 16.50 0.00 2.02 700    
  0.060 1.90 0.45 0.040 0.010 10.30 16.90 0.30 2.20 900    
316HS 0.040 1.30 0.30 0.000 0.020 10.10 16.50 0.00 2.02 400   CaSi inj must
  0.060 1.50 0.50 0.040 0.030 10.30 16.70 0.30 2.20 600    
316L 0.000 1.20 0.30 0.000 0.000 10.10 16.50 0.00 2.02 550   CaSi inj must
  0.028 1.40 0.50 0.040 0.010 10.40 16.70 0.30 2.20 750    
316LBB 0.000 1.20 0.30 0.000 0.005 10.10 16.10 0.00 2.02 550   CaSi inj must
  0.028 1.40 0.50 0.040 0.015 10.40 16.50 0.30 2.20 750    
316LC 0.000 1.50 0.30 0.000 0.010 10.60 16.50 0.00 2.02 400    
  0.028 1.70 0.50 0.040 0.020 10.90 16.90 0.20 2.20 600    
316LE 0.000 1.20 0.25 0.000 0.000 11.10 16.80 0.00 2.02 200    
  0.028 1.40 0.45 0.040 0.010 11.40 17.20 0.30 2.20 350    
316LEHS 0.000 1.20 0.25 0.000 0.020 11.10 16.80 0.00 2.02 200   CaSi inj must
  0.028 1.40 0.45 0.040 0.030 11.40 17.20 0.30 2.20 350    
316LER Msi-RR 0.000 1.70 0.35 0.000 0.000 12.60 18.60 0.00 2.22 400   P+S = 0.03 max.
  0.018 1.90 0.50 0.020 0.010 12.80 18.90 0.15 2.40 600   Co = 0.15 max
316LER Msi-VW 0.000 1.70 0.35 0.000 0.000 13.10 19.10 0.00 2.52 600   P+S= 0.03 max
  0.018 1.90 0.50 0.020 0.010 13.40 19.40 0.15 2.70 800   Co = 0.15 max
316LG 0.000 1.40 0.30 0.000 0.010 10.20 16.50 0.00 2.02 600   CaSi inj must
  0.028 1.60 0.50 0.040 0.020 10.40 16.70 0.30 2.20 800    
316LGHS 0.000 1.40 0.30 0.000 0.020 10.20 16.50 0.00 2.02 600   CaSi inj must
  0.028 1.60 0.50 0.040 0.030 10.40 16.70 0.30 2.20 800    
316LHS 0.000 1.20 0.30 0.000 0.020 10.10 16.50 0.00 2.02 550    
  0.028 1.40 0.50 0.040 0.030 10.40 16.70 0.30 2.20 750    
316LHSCu 0.000 1.20 0.30 0.000 0.020 10.10 16.50 0.40 2.02 550   CaSi inj must
  0.028 1.40 0.50 0.040 0.030 10.40 16.70 0.60 2.20 750    
316LK 0.015 1.30 0.25 0.000 0.010 11.10 17.00 0.00 2.10 600   CaSi inj must
  0.030 1.50 0.40 0.040 0.020 11.30 17.30 0.30 2.20 800    
316LMER 0.000 1.50 0.30 0.000 0.000 10.50 16.50 0.00 2.02 550   Co  0 .05 max
  0.018 1.70 0.50 0.040 0.010 10.70 16.70 0.30 2.20 750    
316LMS 0.000 1.20 0.30 0.000 0.007 10.10 16.50 0.00 2.02 550   CaSi inj must
  0.028 1.40 0.50 0.040 0.017 10.40 16.70 0.30 2.20 750    
316LRHS 0.000 1.20 0.30 0.000 0.020 11.10 16.80 0.00 2.02 250   CaSi inj must
  0.028 1.40 0.50 0.040 0.030 11.40 17.20 0.30 2.20 350    
316LSP 0.020 1.30 0.30 0.000 0.000 10.10 16.50 0.00 2.02 400    
  0.028 1.50 0.45 0.040 0.010 10.40 16.70 0.30 2.20 600    
316LU 0.000 1.20 0.30 0.000 0.000 11.10 16.50 0.00 2.02 0    
  0.028 1.40 0.50 0.030 0.010 11.40 16.70 0.30 2.20 350    
316NG 0.030 1.30 0.25 0.000 0.000 10.30 16.60 0.00 2.02 500    
  0.050 1.50 0.45 0.040 0.020 10.50 16.90 0.30 2.20 700    
316NMHSCu 0.040 1.70 0.25 0.000 0.020 10.10 16.50 0.40 2.02 700   CaSi inj must
  0.060 1.90 0.45 0.040 0.030 10.30 16.80 0.60 2.20 900    
316RU 0.050 1.20 0.25 0.000 0.000 10.60 16.60 0.00 2.02 250    
  0.070 1.40 0.45 0.030 0.010 10.90 17.00 0.30 2.20 450    
316Ti 0.020 1.50 0.30 0.000 0.000 11.00 16.60 0.00 2.02 0 Ti Al = .03/.05
  0.040 1.70 0.50 0.040 0.010 11.40 17.00 0.30 2.20 200 0.15/.25 Ti = 5x %C min
317LN 0.020 1.00 0.45 0.000 0.000 13.80 18.00 0.00 4.10 1100   CaSi inj must
  0.030 1.30 0.60 0.040 0.010 14.00 18.30 0.25 4.30 1300    
321 0.000 1.60 0.30 0.000 0.010 9.30 17.10 0.00 0.00 0 Ti Al = .03/.05
  0.030 1.80 0.45 0.040 0.020 9.50 17.40 0.30 0.30 200 .30/.40 Ti = 5x%(C+N) min
321SP 0.020 1.00 0.30 0.000 0.000 10.50 18.10 0.00 0.00 0 Ti Al = .03/.05
  0.040 1.20 0.50 0.040 0.010 10.80 18.40 0.30 0.15 200 .10/.18 Ti = 5x %C min
321SPL 0.030 1.60 0.30 0.000 0.000 9.40 17.10 0.00 0.00 0 Ti Al = .03/.05
  0.050 1.80 0.45 0.025 0.010 9.60 17.40 0.30 0.30 200 .50/.60 Ti = 0.50 min
405 0.040 0.75 0.40 0.000 0.000 0.00 11.60 0.00 0.00 0 Al  
  0.060 0.90 0.60 0.040 0.010 0.25 12.00 0.25 0.15 200 .12/.18  
409Ti 0.000 0.40 0.30 0.000 0.000 0.75 11.00 0.00 0.00 0   Ti = 16 X %C min
  0.025 0.60 0.50 0.040 0.030 1.00 11.40 0.20 0.20 200    
410 0.100 0.60 0.30 0.000 0.010 0.00 12.50 0.00 0.00 0   CaSi inj must
  0.120 0.85 0.50 0.040 0.020 0.25 13.00 0.30 0.30 200    
410B/403 0.100 0.60 0.30 0.000 0.010 0.00 12.50 0.00 0.00 0   CaSi inj must
  0.120 0.85 0.50 0.040 0.020 0.25 13.00 0.30 0.30 200    
410G 0.080 0.60 0.40 0.000 0.000 0.00 13.10 0.00 0.00 0   CaSi inj must
  0.100 0.85 0.60 0.040 0.015 0.25 13.40 0.30 0.30 200    
410HS 0.100 0.60 0.40 0.000 0.020 0.00 12.50 0.00 0.00 0   CaSi inj must
  0.120 0.85 0.60 0.040 0.030 0.25 13.00 0.30 0.30 200    
410SP 0.040 0.75 0.40 0.000 0.000 0.00 12.00 0.00 0.00 0   CaSi inj must
  0.060 0.90 0.60 0.030 0.010 0.25 12.50 0.25 0.15 200    
410VS 0.130 0.60 0.40 0.000 0.020 0.00 12.50 0.00 0.00 0   CaSi inj must
  0.150 0.85 0.60 0.040 0.030 0.25 13.00 0.30 0.30 200    
410W 0.080 0.60 0.40 0.000 0.000 0.00 12.50 0.00 0.00 0   CaSi inj must
  0.100 0.85 0.60 0.040 0.020 0.25 13.00 0.30 0.30 200    
416 0.120 1.10 0.40 0.000 0.290 0.00 12.20 0.00 0.00 0    
  0.140 1.20 0.60 0.040 0.330 0.25 12.60 0.30 0.30 200    
416V 0.120 1.10 0.20 0.000 0.150 0.00 12.20 0.00 0.00 0    
  0.150 1.20 0.40 0.040 0.200 0.25 12.60 0.30 0.30 200    
416XM 0.100 1.10 0.40 0.000 0.310 0.00 12.20 0.00 0.00 0   CaSi inj must
  0.120 1.20 0.60 0.040 0.340 0.25 12.60 0.25 0.25 200    
420 0.150 0.60 0.40 0.000 0.000 0.00 12.20 0.00 0.00 0    
  0.180 0.85 0.60 0.040 0.020 0.25 12.60 0.30 0.30 200    
420G 0.200 0.60 0.40 0.000 0.020 0.50 13.00 0.00 0.00 0    
  0.220 0.85 0.60 0.040 0.030 0.70 13.50 0.30 0.30 200    
420VS 0.200 0.60 0.40 0.000 0.020 0.00 12.70 0.00 0.00 0   CaSi inj must 
  0.220 0.85 0.60 0.040 0.030 0.25 12.90 0.30 0.30 200    
430F 0.050 1.10 0.40 0.000 0.250 0.00 16.10 0.00 0.00 0    
  0.070 1.25 0.60 0.040 0.290 0.25 16.40 0.30 0.30 200    
430FDIN 0.120 1.30 0.40 0.000 0.250 0.00 15.60 0.00 0.22 0   CaSi inj must
  0.150 1.50 0.60 0.040 0.290 0.25 16.10 0.30 0.30 200    
430K 0.030 0.35 0.30 0.000 0.000 0.00 16.20 0.00 0.00 0    
  0.050 0.50 0.50 0.040 0.030 0.25 16.60 0.30 0.30 250    
430KS 0.030 0.35 0.30 0.000 0.000 0.00 16.60 0.00 0.00 0    
  0.050 0.50 0.50 0.040 0.010 0.50 16.90 0.30 0.30 250    
430L 0.000 0.35 0.30 0.000 0.000 0.00 16.60 0.00 0.00 150    
  0.025 0.50 0.50 0.035 0.010 0.25 16.90 0.30 0.30 300    
430USA 0.000 0.35 0.30 0.000 0.000 0.00 16.50 0.00 0.00 0    
  0.030 0.50 0.50 0.035 0.010 0.05 16.90 0.30 0.30 200    
431HS 0.130 0.60 0.30 0.000 0.020 1.35 15.50 0.00 0.00 0   CaSi inj must
  0.160 0.80 0.50 0.040 0.030 1.50 16.00 0.30 0.30 200    
431VHS 0.130 0.60 0.30 0.000 0.020 2.00 15.70 0.00 0.00 0    
  0.150 0.80 0.50 0.040 0.030 2.20 16.20 0.30 0.30 200    
434 0.030 0.40 0.40 0.000 0.020 0.00 16.40 0.00 0.90 0   CaSi inj must
  0.000 0.30 0.30 0.000 0.000 0.00 16.30 0.85 0.00 0    
434A 0.030 0.50 0.50 0.035 0.010 0.25 16.50 1.00 0.30 250    
  0.050 0.60 0.60 0.040 0.030 0.30 16.80 0.30 1.10 200    
AISI201 0.080 7.10 0.40 0.000 0.000 3.60 16.10 0.30 0.00 1400    
  0.100 7.40 0.60 0.060 0.010 3.80 16.40 0.50 0.30 1600    
AISI202 0.080 7.50 0.50 0.000 0.000 4.10 17.10 0.00 0.00 1400    
  0.100 8.00 0.70 0.060 0.015 4.60 17.50 0.30 0.30 1600    
SI3DM 0.060 9.00 0.40 0.000 0.000 1.80 15.00 1.70 0.00 1400   Aim Ni eqv >12
  0.080 9.40 0.60 0.070 0.015 2.00 15.40 1.90 0.30 1600    
TP 316Ti 0.015 1.60 0.30 0.000 0.000 11.80 16.60 0.00 2.02 0 Ti Al = .025/.045
  0.030 1.80 0.50 0.040 0.010 12.00 16.80 0.50 2.20 200 0.20/.30 Ti= 5x%(C+N2)min
TP304H 0.040 1.70 0.25 0.000 0.000 8.50 18.30 0.00 0.00 700    
  0.060 1.90 0.45 0.040 0.010 8.70 18.60 0.30 0.30 900    
TP304L 0.000 1.20 0.30 0.000 0.000 10.20 18.30 0.00 0.00 600    
  0.020 1.40 0.45 0.035 0.010 10.40 18.60 0.30 0.30 800    
TP316H 0.040 1.30 0.25 0.000 0.000 11.10 16.50 0.00 2.02 400    
  0.060 1.50 0.40 0.040 0.010 11.40 16.80 0.50 2.20 600    
TP316L 0.000 1.20 0.25 0.000 0.000 11.40 16.80 0.00 2.02 250    
  0.028 1.40 0.45 0.040 0.010 11.80 17.20 0.30 2.20 350    
TP410S 0.040 0.55 0.35 0.000 0.000 0.00 12.10 0.00 0.00 0    
  0.060 0.70 0.50 0.035 0.010 0.25 12.50 0.20 0.20 200    
XX 0.000 0.00 0.00 0.000 0.000 0.000 0.000 0.00 0.000 0.000 0.000 0.000
  0.000 0.00 0.00 0.000 0.000 0.000 0.000 0.00 0.000 0.000 0.000 0.000
 

 

 

 